牌號(hào)
|
30SiMn2MoVA合金結(jié)構(gòu)鋼絲
|
|
|
|
|
|
|
|
|
|
|
中國(guó)ISC
|
A14303
|
|
|
|
|
|
|
|
|
|
|
對(duì)應(yīng)標(biāo)準(zhǔn)
|
GB /T 3079-1993
|
|
|
|
|
|
|
|
|
|
|
合金結(jié)構(gòu)鋼絲
|
|
|
|
|
|
|
|
|
|
|
Alloy structure steels wires
|
|
|
|
|
|
|
|
|
|
|
歸類
|
合金鋼
|
|
|
|
|
|
|
|
|
|
|
30SiMn2MoVA 化學(xué)元素成分含量(%)
|
|
|
|
|
|
|
|
|
|
|
|
成分
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Ni
|
Cu
|
Mo
|
V
|
|
最小值
|
0.27
|
0.4
|
1.6
|
-
|
-
|
-
|
-
|
-
|
0.4
|
0.15
|
|
最大值
|
0.33
|
0.6
|
1.85
|
0.025
|
0.025
|
0.25
|
0.25
|
0.25
|
0.6
|
0.25
|
|
特級(jí)優(yōu)質(zhì)鋼 P≤0.025%，S≤0.015%，此時(shí)在鋼號(hào)后加E。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
GB 30SiMn2MoVA GB/T 3079 Mechanical
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Yield
|
Tensile
|
Impact
|
Elongation
|
Reduction in cross section on fracture
|
As-Heat-Treated Condition
|
Brinell hardness (HBW)
|
|
|
|
|
|
Rp0.2 (MPa)
|
Rm (MPa)
|
KV/Ku (J)
|
A (%)
|
Z (%)
|
|
|
|
|
|
423 (≥)
|
717 (≥)
|
24
|
34
|
14
|
Solution and Aging, Annealing, Ausaging, Q+T,etc
|
123
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
GB 30SiMn2MoVA GB/T 3079 Physical
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
GB 30Si Mn2Mo VA GB/T 3079的物理性能參數(shù)主要由GB 30Si Mn 2Mo VA GB/T3079的導(dǎo)熱系數(shù)、比熱容、彈性模量、熱膨脹系數(shù)、電阻值、密度、泊松比等參數(shù)表示。
|
|
|
|
|
|
|
|
|
|
|
|
Temperature
|
Modulus of elasticity
|
Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) and
|
Thermal conductivity
|
Specific thermal capacity
|
Specific electrical resistivity
|
Density
|
Poisson’s coefficient, ν
|
|
|
|
|
(°C)
|
(GPa)
|
(W/m·°C)
|
(J/kg·°C)
|
(Ω mm2/m)
|
(kg/dm3)
|
|
|
|
|
24
|
-
|
-
|
|
|
0.13
|
-
|
|
|
|
|
|
564
|
374
|
-
|
21.3
|
131
|
|
-
|
|
|
|
|
|
467
|
-
|
12
|
34.2
|
|
|
112
|
214
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|