牌號(hào)
|
1.1269彈簧鋼、冷軋窄鋼帶
|
|
|
|
|
|
|
|
|
德國W-Nr.
|
C85S
|
|
|
|
|
|
|
|
|
對(duì)應(yīng)標(biāo)準(zhǔn)
|
DIN EN 10132-4-2000(+AC:2002)/EN/JIS
|
|
|
|
|
|
|
|
|
熱處理?xiàng)l件下的冷軋窄鋼帶 - 交貨技術(shù)條件 - 第4部分：彈簧鋼和其它用途，勘誤2002
|
|
|
|
|
|
|
|
|
Cold-rolled narrow steel strip for heat treatment-Technical delivery conditions Part 4: Spring steels and other applications (includes Corrigendum AC:2002)
|
|
|
|
|
|
|
|
|
歸類
|
彈簧鋼
|
|
|
|
|
|
|
|
|
1.1269化學(xué)元素成分含量(%)
|
|
|
|
|
|
|
|
|
|
成分
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Ni
|
Mo
|
|
最小值
|
0.8
|
0.15
|
0.4
|
-
|
-
|
-
|
-
|
-
|
|
最大值
|
0.9
|
0.35
|
0.7
|
0.025
|
0.025
|
0.4
|
0.4
|
0.1
|
|
|
|
|
|
|
|
|
|
|
|
1.1269機(jī)械性能
|
|
|
|
|
|
|
|
|
|
厚度
|
熱處理或狀態(tài)
|
抗拉強(qiáng)度
|
屈服點(diǎn)
|
斷后伸長率或延伸率
|
硬度
|
|
|
|
|
t
|
σb
|
σs
|
δ
|
HBW
|
|
|
|
|
mm
|
Mpa
|
Mpa
|
%
|
|
|
|
|
|
0.3≤t≤3
|
退火(+A)或退火平整(+LC)
|
≤670
|
≤535
|
≥15
|
HV
|
|
|
|
|
≤210
|
|
|
|
|
0.3≤t≤3
|
冷軋（+CR）
|
≤1190
|
|
|
≤325
|
|
|
|
|
0.3≤t≤3
|
調(diào)質(zhì)（+QT）
|
1200~2000
|
|
|
370~600
|
|
|
|
|
①客戶可以硬度或抗拉強(qiáng)度值，但不能同時(shí)。如果兩者都沒有，則應(yīng)適用抗拉強(qiáng)度值。
|
|
|
|
|
|
|
|
|
|
②對(duì)于厚度更厚的帶材，其機(jī)械性能應(yīng)在訂貨或詢價(jià)時(shí)商定。
|
|
|
|
|
|
|
|
|
|
③對(duì)于冷軋狀態(tài)交貨的材料，強(qiáng)度范圍150MPa 或硬度范圍50HV應(yīng)適用，例如:850 MPa~1000 MPa或如240 HV~290 HV。
|
|
|
|
|
|
|
|
|
|
④對(duì)于在淬火和回火條件下供應(yīng)的材料，范圍為150 MPa 或50 HV應(yīng)適用，如1350 MPa ~1500 MPa 或如450 HV~500 HV。
|
|
|
|
|
|
|
|
|